초록
[ $TiO_2-Nb_2O_5$ ] sol was prepared using sol-gel method. Crystalline properties of gel powder changed from rutile phase to anatase phase with increasing $Nb_2O_5$ additives at $800^{\circ}C$, while they retained rutile phase regardless of $Nb_2O_5$ additives at $900^{\circ}C,\;1,000^{\circ}C$. They retained amorphous phase from $50^{\circ}C\;to\;400^{\circ}C$, retained anatase phase from $500^{\circ}C\;to\;600^{\circ}C$ and had rutile phase over $700^{\circ}C$ at 1mole% $Nb_2O_5$ additive. After $TiO_2-Nb_2O_5$ sol retained low viscosity with normal chain structure for a long time, its viscosity increased fast with network structure. DTA properties of gel powder had endothermic reaction due to evaporation of propanol and water about $78^{\circ}C$, had exothermic reaction due to propanol combustion about $290^{\circ}C$ and had exothermic reaction due to changing of $TiO_2$ phase about $640^{\circ}C$.