Thermal Expansion and Dielectric Properties of CaO-ZnO-B2O3-SiO2 Glass-Added Al2O3 Composites for LTCC Applications

  • Byeon, Tae-Hun (Department of Advanced Ceramic Materials Engineering, Gangneung-Wonju National University) ;
  • Park, Hyo-Sung (Department of Advanced Ceramic Materials Engineering, Gangneung-Wonju National University) ;
  • Shin, Hyun-Ho (Department of Advanced Ceramic Materials Engineering, Gangneung-Wonju National University) ;
  • Yoon, Sang-Ok (Department of Advanced Ceramic Materials Engineering, Gangneung-Wonju National University) ;
  • Oh, Chang-Yong (Temen Technology, Inc., Gangneung Science Industry Park)
  • Received : 2010.03.03
  • Accepted : 2010.06.08
  • Published : 2010.07.31
Download PDF
⟨ Previous Next ⟩

Abstract

Varying quantities of a high-thermal-expansion glass, 50CaO-20ZnO-$20B_2O_3-10SiO_2$ (CZBS), were added to alumina and sintered at $875^{\circ}C$ for 2 h for low temperature co-firing ceramic (LTCC) applications. As the amount of glass addition increased from 40 wt% to 70 wt%, the apparent density of the sintered product increased from 88.8% to 91.5%, which was also qualitatively confirmed by microstructural observation. When the glass addition was very high, e.g., 70 wt%, an apparent formation of secondary phases such as $CaZn_2AlZnSiAlO_7$, $Ca_2Al(AlSi)O_7$, $Ca_2Al_2SiO_7$, $Ca_2ZnSi_2O_7$ and ZnO, was observed. Both the dielectric constant and the coefficient of thermal expansion increased with the glass addition, which was qualitatively consistent with the analytical models, while the experimental values were lower than the predicted ones due to the presence of pores and secondary phases.

Keywords

References

  1. N. T. Cho, K. B. Shimb, S. W. Lee, and K. D. Koo, “Fabrication of Low-temperature Co-Fired Ceramic (LTCC) Chip Couplers for High Frequencies: II. Effect of Binder Burnout Process on the Formation of Electrode Line,” J. Kor. Ceram. Soc., 36 [6] 583-89 (1999).
  2. S.W. Lee, K.H. Kim, K. B. Shimb, and K. D. Koo, “Fabrication of Low-temperature Co-Fired Ceramic (LTCC) Chip Couplers for High Frequencies: II. Effect of Sintering Process on Ag Diffusion(in Korean),” J. Kor. Ceram. Soc., 36 [5] 490-96 (1999).
  3. Y. Cho and K. W. Hang, ‘‘High Thermal Expansion Glass and Tape Composition,” US Patent 6835682, 2003.
  4. N. Hamada, H. Yonekura, K. Nagae, Y. Furukubo, Y. Nakao, and M. Higashi, "High-Thermal-Expansion Glass Ceramic Sintered Product, US Patent 6348427, 2002.
  5. A. A. Appen, “Versuch zur Klassfizierung von Komponenten nach ihrem Einflu${\beta}$‚ auf die Oberflachenspannung von Silikatschmelzen,” Silikattechnik, 5 11-3 (1954).
  6. J. S. Park, Y. Kim, H. Shin, J.H. Moon, and W. Lim “Calcium Zinc Borosilicate Glass with High Thermal Expansi on Coefficient for LTCC Application,” J. Am. Ceram. Soc., 91 [11] 3630-33 (2008). https://doi.org/10.1111/j.1551-2916.2008.02732.x
  7. W. D. Kingery, H. K. Bowen, and D. R. Uhlmann, Introduction to Ceramics 2nd Ed., p. 604, John Wiley & Sons (Asia) Ltd., Singapore ,1976.
  8. H. Shin, J.-S. Park, S.-G. Kim, H. S. Jung, K. S. Hong, and H. Kim, “Role of Submicron Residual Fillers in Improving Optical Reflectance of Barrier Rib Glasses for Plasma Display Panels,” J. Mater. Res., 21 [7] 1753-58 (2006). https://doi.org/10.1557/jmr.2006.0205
  9. S-.G. Kim, J.-S. Park, J.-S. An, K. S. Hong, H. Shin, and H. Kim, “Effects of the Addition of Different Types of Fillers on the Properties of $BaO-ZnO-B_{2}O_{3}-SiO_{2}$ Glass Composites for Application to Barrier Ribs of Plasma Display Panels,” J. Am. Ceram. Soc., 89 [ 3] 902-7 (2006). https://doi.org/10.1111/j.1551-2916.2005.00805.x
  10. MatWeb Material Property Data, http://www.matweb.com/
  11. W. D. Kingery, H. K. Bowen, and D. R. Uhlmann, Introduction to Ceramics 2nd Ed., p. 947, John Wiley & Sons (Asia) Ltd., Singapore ,1976.

Cited by

  1. Low-Temperature Sintering and Microwave Dielectric Properties of MgO Ceramic with LiF Addition vol.50, pp.9, 2011, https://doi.org/10.1143/JJAP.50.09NF02
  2. Crystal structure and microwave dielectric properties of low temperature sintered MgO ceramic with LiF addition pp.2044-5326, 2012, https://doi.org/10.1557/jmr.2011.438
  3. Low-temperature sintering and microwave dielectric properties of LiF-doped 0.2Li2ZrO3–0.8MgO ceramics vol.29, pp.16, 2018, https://doi.org/10.1007/s10854-018-9505-2