Abstract
This study was carried out for the purpose of improving driving safety and comfort of the railways quickly becoming popular. To conducted gas pressure welding to ensure the strength safety of continuous welded rail and rotating bending test tensile test was conducted. The element to determine the tensile strength of gas pressure welds at experiments be attributed to more upsetting length than pressure, according to increases of upsetting length, from brittle fracture to ductile fracture was observed. Through the biopsy of the fracture surface, according to the presence of brittle fracture could be evaluated to strength safety. In addition, mechanical strength of gas pressure welding depending on changes in upsetting length was different. Rotary bending test results were obtained to the infinite life according to exhibited higher fatigue limit of 373MPa at upsetting length 25mm.
본 연구는 빠르게 대중화 되어가는 철도의 주행안전성과 승차감 개선을 목적으로 수행하였다. 가스압접을 실시하는 장대레일의 강도 안전성을 확보하기 위하여 인장시험과 회전굽힘시험을 실시했다. 실험을 통하여 가스 압접부의 인장강도를 결정하는 요소는 가해진 압력보다 업셋길이의 변화에 기인하며, 업셋길이가 늘어남에 따라서 취성파괴에서 연성파괴가 발생하는 것을 관찰했다. 파단면의 조직검사를 통해 그 면에 존재하는 취성파면의 유무에 따라서 강도 안전성을 용이하게 평가할 수 있었다. 회전굽힘시험 결과 업셋길이 25mm에서 373MPa의 우수한 피로한도가 나타났으며, 무한수명을 얻을 수 있었다.