Abstract
This research is based on fabricating Cu(In,Ga)$Se_2$ thin-film by co-evaporation method. On $1^{st}$ - stage, $In_2Se_3$ phase appeared when the substrate temperature reached to $400^{\circ}C$, however, there was small effect between the substrate temperature and absorbency spectrum on $2^{nd}$, $3^{rd}$ - stage because the average thickness of the thin-film was $1{\mu}m$ or higher. SEM and XRD was measured on $2^{nd}$ and $3^{rd}$ stage and it showed as the substrate temperature increases, the density of the crystal structure increased with the decreament of the vacancy. Furthermore, the formation of Cu(In0.7Ga0.3)$Se_2$ phase showed at $480^{\circ}C$ and $500^{\circ}C$.
동시진공증발법(co-evaporation)으로 Cu(In,Ga)$Se_2$ 박막을 제작하는 논문으로서 1단계($1^{st}$-stage)에서 기판온도(substrate temperature)가 $400^{\circ}C$에서 $In_2Se_3$상($In_2Se_3$ phase)이 존재하였으며 2,3단계($2^{nd}$-stage, $3^{rd}$-stage)에서 기판온도 변화에 따른 흡수 스펙트럼(absorbency spectrum)은 차이가 크지 않다. 이것은 박막의 두께가 전부 $1{\mu}m$ 이상이므로 흡수 스펙트럼(absorbency spectrum)은 거의 차이가 없다. 2,3단계에서 기판온도 변화에 따른 SEM과 XRD를 분석한 결과, 기판온도가 증가할수록 결정구조(crystal structure)의 밀도(density)가 증가하고 기공(vacancy)이 감소하며 $480^{\circ}C$, $500^{\circ}C$에서 Cu(In0.7Ga0.3)$Se_2$상(${\mu}m$)이 형성되었다.