초록
Generally, the color gold has had a biased conception due to its traditional use. Thus, this bias has resulted in a lack of usage of golden glaze on ceramics and also a lack of extensive studies of such glazes. In this paper, optimum conditions and mechanism of formation of gold color crystallization glaze containing $Fe_2O_3$(hematite), which is developed for gold colors of ceramic glazes, were studied. Experimental result showed that there are pyroxene based on diopside and $TiO_2$ phase in the base of a crystallization glaze with a value of $TiO_2$ of 6 wt% confirmed by XRD and Raman Spectroscopy. When $Fe_2O_3$ was used as a colorant for the gold color, the $TiO_2$ peak became extinct and the intensity of the diopside peak was sharper. Feldspar of 60 wt%, talc of 20 wt% and limestone of 20 wt% were used as the starting materials and these were tested using a three component system. The best result of test was selected and extended to its vicinity as an experiment to determine $TiO_2$ and $Fe_2O_3$ contents. The glaze with $TiO_2$ of 6 wt% and $Fe_2O_3$ of 12 wt% addition showed stable pyroxene based diopside crystals and the development of gold color. This gold color was obtained with CIE-$L^*a^*b^*$ values of 51.27, 4.46, 16.15 (a grayish yellow brown color), which was gained using the following firing conditions: temperature increasing speed $5^{\circ}C$/min, holding for 1 h at $1280^{\circ}C$, annealing speed $3^{\circ}C$/min till $1100{\circ}C$, holding for 2 h at $1100{\circ}C$, and finally natural annealing.