Carburization Characteristics of MERT Type KHR-45A Steel in Carbon Rich Environment

Carbon Rich 분위기에서의 KHR45강의 침탄특성 평가 연구

  • Received : 2013.04.15
  • Accepted : 2013.05.08
  • Published : 2013.05.27

Abstract

In this study, an HP-mod. type(KHR-45A), which is used as a heater tube material in the pyrolysis process, was evaluated for its carburizing properties. It was confirmed from the microstructural observation of the tubes that the volume fraction of carbide increased and that the coarsening of Cr-carbide generated as a degree of carburization increased. The depth of the hardened layer, which is similar to the thickness of the carburized region of each specimen, due to carburization is confirmed by measurement of the micro-Vickers hardness of the cross section tube, which thickness is similar to that of the carburized region of each specimen. Two types of chromium carbides were identified from the EBSD (electron back-scattered diffraction) image and the EDS (energy-dispersive spectroscopy) analysis: Cr-rich $M_{23}C_6$ in the outer region and Cr-rich $M_7C_3$ in the inner region of tubes. The EDS analysis revealed a correlation between the ferromagnetic behavior of the tubes and the chromium depletion in the matrix. The chromium depletion in the austenite matrix is the main cause of the magnetization of the carburized tube. The method used currently for the measurement of the carburization of the tubes is confirmed; carburizing evaluation is useful for magnetic flux density measurement. The volume fraction of the carbide increased as the measuring point moved into the carburized side; this was determined from the calculation of the volume fraction in the cross-section image of the tubes. These results are similar to the trends of carburization measurement when those trends were evaluated by measurement of the magnetic flux density.

Keywords

References

  1. LH Almeida, AF Ribeiro, IL May, Materials Characterization 49, 219-229 (2003).
  2. Shinoda TL, Zaghloul MB, Kondo Y, Tanaka R. Trans Iron Steel Inst. Jpn. 18, 139-148 (1998).
  3. Borges RMT, de Almeida LH. Acta Microsc Suppl A, 8, 251-252 (1999).
  4. Y. V. Nawancy, Engineering Failure Analysis 16, 2171-2178 (2009). https://doi.org/10.1016/j.engfailanal.2009.02.009
  5. I. C. Silva, J. M. A. Rebello, A. C. Bruno, P. J. Jacques, B. Nystend and J. Dillee, Scripta Materialia 59, 1010-1013 (2008). https://doi.org/10.1016/j.scriptamat.2008.07.015
  6. UL-HAMAD, H. M. TAWANCY, S. S AL-JAROUND, A. I. MOHAMMED, N. M. ABBAS. Material Science-Poland, Vol. 24, No.2/1, (2006).
  7. Stevens KJ, Tack AJ, Thomas CW, Stewart D. J Phys D 34, 814-822 (2001). https://doi.org/10.1088/0022-3727/34/5/320
  8. H. J. Grabke Materials at High Temperature 17, 483 (2000). https://doi.org/10.1179/mht.2000.063
  9. K. J. Stevens, A. Parbhu, J. Soltis, D. Stewart, Journal of Physics D: Applied Physics 36, 164 (2003). https://doi.org/10.1088/0022-3727/36/2/315

Cited by

  1. Deformation Properties of TiC-Mo Eutectic Composite at High Temperature vol.23, pp.10, 2013, https://doi.org/10.3740/MRSK.2013.23.10.568