Abstract
In this study, based on CMA which is increasingly used for eco-friendly deicing materials, dehumidification MB made of sodium carbonate, $MgCl_2$/MgO (M/M), and SAP is to be produced. And its moisture absorption rate and dehumidification performance of the film are to be analyzed. And the data on the materials used for the dehumidification film are to be acquired. In case of the dehumidification MB, in which CMA and SAP are mixed, had poor film machinability due to foaming and moisture issues, but adding bentonite and calcium carbonate solved the problem. When a foaming agent was added to extend surface area between substances, CMA and M/M showed no remarkable difference, but SC showed large increase to 3.15 g/g. As the result of anti-corrosive test, CMA dehumidification film showed no corrosion while SC showed pitting corrosion and M/M showed corrosion.
본 연구에서는 친환경 제설제로 사용이 증가되고 있는 CMA를 바탕으로 고성능흡습제로 사용되어지고 있는 SAP와 sodium carbonate, $MgCl_2$/MgO (M/M)에 대하여 제습MB를 제조하고 필름으로서의 흡습율 및 제습성능을 분석하고, 제습필름 적용물질에 대한 Data를 확보하고자 한다. CMA와 SAP를 혼합한 제습MB의 경우 발포현상과 수분문제로 필름가공성이 어려웠으나, Bentonite와 calcium carbonate 첨가로 해결할 수 있었다. 필름가공시 물질들 간의 표면적 공간을 넓히는 역할로서 발포제를 첨가한 경우, CMA와 M/M의 경우 큰 차이성은 없었지만, 발포제가 첨가된 SC의 제습성은 3.15 g/g로 높은 결과를 알 수 있었다. 또한 방청성 테스트의 결과 CMA 제습필름 경우 부식발생은 없었으며, SC의 경우 점 부식 발생, M/M의 경우 부식발생이 일어났다.