Abstract
The internal chromium plating of a long-axis tube is widely used in military and industrial application, with the thick hard plating formed using a mixed solution of Chromium acid and catalytic $H_2SO_4$. A large-caliber gun can endure a high explosive force as a result of the increased stiffness and wear resistance provided by this internal hard chromium surface. The internal chromium layer of a tube is prone to exfoliation caused by the high kinetic energy of the projectile and high pressure of the explosion. Therefore, we reviewed the plating process. Chromium plating comprises many steps, including the removal of Grease, water cleaning, electrolytic abrasion, etching, plating, water cleaning, and hydrogen brittleness removal. The exfoliated chromium plating layer is affected by the adhesion property of the plating. In particular, the Fe concentration of the electrolyte affects the adhesion property. The optimum Fe concentration for effectively suppressing the exfoliation of the plating layer was established by using a scanning electron microscope to determine the surface roughness, and the effectiveness was proved in an adhesion test, etc.
장축의 내부 크롬도금은 크롬산 용액에 황산을 촉매로 경질의 후막 도금층을 형성시키는 기술로서 산업뿐만 아니라 군사적 목적으로도 널리 사용되고 있다. 대구경의 포신내부에 경질크롬도금을 처리하면 강성과 내마성을 증대시켜 고압의 폭발력에 견딜 수 있다. 탄자의 높은 운동에너지와 탄 폭발로 생긴 고압력에 의해 포신 내부의 크롬도금층이 탈락되는 문제가 있어 도금 공정 전반에 걸친 검토가 이루어졌다. 크롬도금은 탈지, 수세, 전해연마, 에칭, 도금, 수세 및 수소취성제거 등 여러 공정으로 이루어진다. 크롬도금 탈락은 도금의 밀착성과 연관이 있으며, 그 중에 전해연마액의 Fe 농도가 도금 밀착성에 영향을 미치는 것으로 나타났다. 도금부위의 요철상태를 SEM으로 조사하여 도금탈락을 방지할 수 있는 최적의 Fe 농도를 설정하고, 밀착성 시험 등으로 그 효과를 입증하였다.