This study analyzes the environmental and durability problems of traditional (LW) grouting method. And the proposed method was compared to the others effects by analyzing the in-situ applicability and effect of performance of the method using the silica sol. This study analyzed the eco-friendly, effects of high strength silica sol through laboratory tests. The effects of the construction process were identified through the field tests. The compressive strength was increased by 1.3 times compared to the LW method and the shrinkage is 3~8 times less than that of LW method with water glass. No toxicity, which could affect soil contamination. In particular, it was confirmed that the Toxicity fish also survived with little pH change in the concentration tank. Also it confirmed the construction effects through field test. Field tests are a standard penetration test, permeability test, LLT, BST. Permeability was reduced to $1{\times}10^{-5{\sim}-6}cm/sec$.
본 연구는 기존 차수 그라우팅공법에서 사용되는 규산질 물유리계(규산소다) 재료에 대해 환경성과 주입재 내구성 문제에 대한 문제점을 인식하여 이를 대체한 실리카졸(Silica-Sol)의 성능효과와 실리카졸을 사용한 공법의 현장 적용성을 분석함으로써 타공법 대비 효과를 비교 제시하였다. 환경성 내구성 평가와 관련 실내에서 주입재에 대한 어독성, 수중불분리 및 pH 농도 변화, 용출, 압축강도, 길이변화(수축량), 해수영향에 의한 약액 효능 분석 시험을 한 결과 실리카졸 공법은 물유리계인 LW 공법에 비해 압축강도는 약 1.3배 강하고 수축률은 3~8배 정도 적었으며, 토양오염에 영향을 줄 수 있는 유해성분(Cd, Cu, Hg, $Cr^{+6}$, 유기인)이 전혀 없는 것으로 나타났다. 특히 어독성의 경우 수조 내 물의 pH 농도 변화가 거의 없이 공시어 또한 모두 장시간 생존하는 것을 확인할 수 있었다. 또한, 해수 염분에 의한 약액의 강도, 내구성 저하가 없는 것으로 분석되었다. 현장시험에서는 주입실시공 후 표준관입시험, 공내재하(LLT), 전단시험(BST)을 통해 지반개량에 대한 강도 물성치 증가 및 현장투수시험을 통해 풍화토(토사)층의 투수계수가 $1{\times}10^{-5{\sim}-6}cm/sec$로 저하됨으로써 현장적용에 대한 공법 시공 효과를 관찰할 수 있었다.