Abstract
In the GTA welding process of Al 7075 alloy using different types of filler metals, the tensile test and micro-hardness test were conducted to evaluate the mechanical characteristics. Also, the radiographic test result showed that the weld met the criterion of level 1 in accordance with KS D 0242 for verifying the welding integrity and there were no welding defects. The tensile test result obtained using Al 7075 as a filler metal showed that the material was fractured in the weld zone. The tensile strengths of the materials using Al 7075 and ER 4043 as the filler metal were about 240MPa and 253MPa, their yield strengths were about 132MPa and 120MPa and their elongation percentages were 6.6% and 13%, respectively. The micro-hardness value of the deposited metal zone when using Al 7075 as the filler metal was Hv 132. However, the micro-hardness of the material using ER4043 as the filler metal was about 24% lower than that using Al 7075. When the chemical composition of the filler metal is the same as that of the material itself, fracture can occur in the deposited metal zone. Therefore, it is not desirable to use the same material as the filler metal for the welding of Al 7075 alloy. Moreover, the use of Al-Si based ER 4043 as a filler metal is more desirable than using the same material as a filler metal for welding Al 7075.
본 연구는 7075 알루미늄 합금의 용가재에 따른 GTA용접공정의 기계적 특성을 평가 하기위해 인장시험, 미세경도 시험과 같은 실험을 실시하였다. 방사선비파괴 시험 결과 KS D 0242규격의 1급의 기준에 만족하였으며 용가재에 따른 용접의 결함증가 등의 문제점은 없는 것으로 판단된다. 인장시험 결과 Al 7075를 용가재로 사용하였을 때에만 용접부에서 파단이 일어났으며 Al 7075, ER 4043의 용가재에 따른 인장강도는 각각 240MPa, 253MPa로 나타나며 항복강도는 각각 132MPa, 120MPa로 나타났으며 연신율은 각각 6.6%, 13%로 나타났다. 미세경도시험 결과 Al 7075를 용가재로 사용했을 때 용착금속부는 경화되어 Hv132로 나타났으며 ER 4043을 사용한 시편의 용착금속부의 경도는 각각 약 24% 감소하여 나타났다. Al 7075의 용접의 경우 같은 합금 조성의 용가재를 사용하여 용접 하면 용착금속부가 경화하여 용착금속부에서 파괴가 일어날 수 있으므로 같은 합금의 조성의 용가재를 사용하지 않는 것이 바람직하다. 위와 같은 실험을 통하여 7075 알루미늄합금의 용접시 같은 합금 조성의 용가재인 Al 7075를 사용하는 것 보다는 Al-Si계인 ER 4043을 용가재를 사용하는 것이 바람직하다.