Investigation of bonding properties of Al/Cu bimetallic laminates fabricated by the asymmetric roll bonding techniques

  • Vini, Mohamad Heydari (Department of Mechanical Engineering, Mobarakeh Branch, Islamic Azad University) ;
  • Daneshmand, Saeed (Department of Mechanical Engineering, Majlesi Branch, Islamic Azad University)
  • 투고 : 2018.07.01
  • 심사 : 2018.12.04
  • 발행 : 2019.01.25

초록

In this study, 2-mm Al/Cu bimetallic laminates were produced using asymmetric roll bonding (RB) process. The asymmetric RB process was carried out with thickness reduction ratios of 10%, 20% and 30% and mismatch rolling speeds 1:1, 1:1.1 and 1:1.2, separately. For various experimental conditions, finite element simulation was used to model the deformation of bimetallic Al/Cu laminates. Specific attention was focused on the bonding strength and bonding quality of the interface between Al and Cu layers in the simulation and experiment. The optimization of mismatch rolling speed ratios was obtained for the improvement of the bond strength of bimetallic laminates during the asymmetric RB process. During the finite element simulation, the plastic strain of samples was found to reach the maximum value with a high quality bond for the samples produced with mismatch rolling speed 1:1.2. Moreover, the peeling surfaces of samples around the interface of laminates after the peeling test were studied to investigate the bonding quality by scanning electron microscopy.

키워드

참고문헌

  1. ASTM-D903-93 (1993), Standard Test Methods for Peel or Stripping Strength of Adhesive Bonds, ASTM International; West Conshohocken, PA, U.S.A.
  2. Chang, H., Zheng, M.Y., Gan, W.M., Wu, K., Maawad, E. and Brokmeier, H.G. (2009), "Texture evolution of the Mg/Al laminated composite fabricated by roll bonding", Scripta Materialia, 61(7), 717-720. https://doi.org/10.1016/j.scriptamat.2009.06.014
  3. Chen, M.C., Hsieh, H.C. and Wu, W. (2006), "The evolution of microstructures and mechanical properties during accumulative roll bonding of Al/Mg composite", Alloys Compound, 416(1-2), 169-172. https://doi.org/10.1016/j.jallcom.2005.09.017
  4. Dassault Systems, ABAQUS/Standard (Version 6.14), https://www.3ds.com/products-services/simulia/products/abaqus/abaqusstandard.
  5. Heydari Vini, M., Daneshmand, S. and Forooghi, M. (2017a), "Roll bonding properties of Al/Cu bimetallic laminates fabricated by the roll bonding technique", Technique, 5(20), 1-10.
  6. Heydari, Vini, Sedighi, M. and Mondali, M. (2017b), "Investigation of bonding behavior of AA1050/AA5083 bimetallic laminates by roll bonding technique", Trans. Indian Inst. Metals, 71(9), 1-6.
  7. Hsieh, P.J., Lo, Y.C., Wang, C.T., Huang, J.C. and Ju, S.P. (2007), "Cyclic transformation between nanocrystalline and amorphous phases in Zr based intermetallic alloys during ARB", Intermetallics, 15(5-6), 644-651. https://doi.org/10.1016/j.intermet.2006.10.031
  8. Hwang, Y.M., Tzou, Y., Hwang, Y.M. and Tzou, G.Y. (1996), "Stress analysis of asymmetrical cold rolling of clad sheet using the slab method", Mater. Eng. Perform., 5(5), 621-631. https://doi.org/10.1007/BF02646092
  9. Jamaati, R. and Toroghinejad, M.R. (2010), "Effect of friction, annealing conditions and hardness on the bond strength of Al / Al strips produced by cold roll bonding process", Mater. Des., 31(9), 4508-4513. https://doi.org/10.1016/j.matdes.2010.04.022
  10. Li, X., Zu, G., Ding, M., Mu, Y. and Wang, P. (2011), "Interfacial microstructure and mechanical properties of Cu / Al clad sheet fabricated by asymmetrical roll bonding and annealing", Mater. Sci. Eng. A, 529, 485-491. https://doi.org/10.1016/j.msea.2011.09.087
  11. Reihanian, M. Bagherpour, E., Paydar, M.H., Reihanian, M., Bagherpour, E. and Paydar, M.H. (2016), "Particle distribution in metal matrix composites fabricated by accumulative roll bonding Particle distribution in metal matrix composites fabricated by accumulative roll bonding", Mater. Sci. Technol., 28(1), 103-108.
  12. Reyds, D., Dyja, H. and Berski, S. (2003), "The prediction of curvature of bimetallic plate Al-Cu during asymmetrical cold rolling", Metalurgija, 42(4), 261-264.
  13. Saito, Y., Utsunomiya, H., Tsuji, N. and Sakai, T. (1999), "Novel ultra-high straining process for bulk materials development of the accumulative roll-bonding (ARB) process", Acta Mater, 47(2), 579-583. https://doi.org/10.1016/S1359-6454(98)00365-6
  14. Sedighi, M., Farhadipour, P. and Heydari Vini, M. (2016), "Mechanical properties and microstructural evolution of bimetal 1050/Al2O3/5083 composites fabricated by warm accumulative roll bonding", Minerals, Metals Mater. Soc., 68(12), 3193-3200. https://doi.org/10.1007/s11837-016-2123-7
  15. Shabani, A., Toroghinejad, M.R. and Shafyei, A. (2012), "Effect of post-rolling annealing treatment and thickness of nickel coating on the bond strength of Al-Cu strips in cold roll bonding process", Mater. Des., 40, 212-220. https://doi.org/10.1016/j.matdes.2012.03.052
  16. Tadanobu, I., Yanagida, A. and Yanagimoto, J. (2013), "Finite element simulation of accumulative roll-bonding process", Mater. Lett., 106, 37-40. https://doi.org/10.1016/j.matlet.2013.04.093
  17. Yan, H. and Lenard, J.G. (2004), "A study of warm and cold roll-bonding of an aluminium alloy", Mater. Sci. Eng. A, 385(1-2), 419-428. https://doi.org/10.1016/S0921-5093(04)00906-2
  18. Yu, H., Tieu, A.K., Lu, C. and Godbole, A. (2014), "An investigation of interface bonding of bimetallic foils by combined accumulative roll bonding and asymmetric rolling techniques", Metallurgical Mater. Trans. A, 45(9), 4038-4045. https://doi.org/10.1007/s11661-014-2311-4
  19. Yu, H., Wang, H., Lu, C., Tieu, A.K., Li, H., Godbole, A. and Kong, C. (2016), "Microstructure evolution of accumulative roll bonding processed pure aluminum during cryorolling", Mater. Res., 31(6), 1-9. https://doi.org/10.1557/jmr.2016.3

피인용 문헌

  1. Two rectangular elements based on analytical functions vol.5, pp.2, 2019, https://doi.org/10.12989/acd.2020.5.2.147