초록
The purpose of this research was th evaluate conductivity of electricity of Ge-Se-Bi system Chalcogenide glass as a amorphous semiconductor by observing its dissolution and crystallization. In this experiment. Ge-Se-Bi metal powder in the rage of $Ge_{12-25}$, $Se_{65-85}$, $Bi_{2.5-15}$ was used as the sample ore. The ore was. put into a vaccous quartz tube and then melted. The condition of heat treatment was to dispose it to $1000^{\circ}C$ heat for 10 hours and then rapidly quenched it at $3834^{\circ}C$/see. The crystallization of the fused sample ripened as the change of temperature and time, after the crystal core was formell. At that time it was possible to observe the state that $Bi_2Se_3$ and $GeSe_2$ were crystallized. In the experiment of making memberance, the memberance was produced by using the previously experimented bulk sample. And decrystalization was well progressed when Ge was over 15 at %, Se was over 70 at %, and Bi was under 10 at%. As for bulk. when Ge was fixed to 20 at %, the conducting of electricity was increased as Bi gained at %. In the case of memberance, the conductivity was much more increased than that of bulk sample as the increase of at the increase of at % of Bi. In the experiment on $Ge_{20}$, $Se_{77.5}$ and $Bi_{2.5}$, the crystallization sswas most vigorous when they were kept at $330^{\circ}C$ for 4 hours.