Abstract
$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$(x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties were investigated with variation of composition ratio and sintering temperature. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $1020^{\circ}C$ due to the formation of the polycrystalline perovskite phase. BSCT(50/40/10) specimen sintered at $1500^{\circ}C$ showed the highest average grain size(18.25$[{\mu}m]$). Curie temperature and dielectric constant at room temperature decreased with increasing amount of Ca. BSCT(50/40/10) specimen sintered at $1450^{\circ}C$ showed a good dielectric constant, K, (=4324) and dielectric loss, $tan{\delta}$, (=0.972%) properties at 1[KHz].