초록
We performed a continuous heat treatment experiment for long Si$_2$Sr$_2$CaCuO$_{x}$ (Bi2212) superconductor tapes on copper substrates. A precursor that contains a mixture of Bi$_2$O$_3$, SrCO$_3$, and CaCO$_3$ powders was prepared and screen-printed on Cu tapes. The screen- printed tapes were thermally treated by consecutive processes with various temperature settings using an air-filled tube furnace. The diffraction patterns and the microstructures of the high temperature superconductor thick films were analyzed by X-ray diffractometry (XRD) and optical Microscopy respectively, and the critical temperatures of the superconducting thick films were measured. The critical temperatures of the superconducting films were measured to be about 77K, and the films'crystallographic c-axes were confirmed to be normal to the film surfaces by XRD and morphology observation. We also observed that the thick superconducting layer is formed and aligned on the copper substrate via partial melted state that consists of a liquid phase and a secondary phase.e.