This study was carried out to investigate the effect of steaming on mechanical properties of heat-compressed wood specimens. The specimens for this mechanical strength tests were prepared to super-heated steam treatment after compression to the radial direction of sonamu (Pinus densiflora). The specimen's size is $50(L)mm{\times}20(R)mm{\times}17(T)mm$. Steaming temperature and treatment time is $120^{\circ}C$ and 20, 40, 60, 80, 100 minutes, respectively. Modulus of elasticity(MOE) in compressive test is directly proportional to steaming time. On the other hand, modulus of elasticity in bending test between steaming and not steaming after heat-compressed wood is similar irrespective of steaming time. The reason for this phenomenon is not clear yet.

This paper describes the bending strength properties of laminated woods which had three kinds of specimens according to finger length-12, 4.5 mm and butt joint and the acoustic emissions (AEs) generated during the test. 3-ply laminated wood beams were tension side layers (lower layers) composed of one middle lamina and two side-jointed laminae, with one butt joint ($_1BJ$), one finger joint (12mm, $_1FJ_{12}$) or one finger joint (4.5mm, $_1FJ_{4.5}$) in the middle lamina of tension side layer. And 3-ply laminated wood beams were tension side layers (lower layers) also composed of one lamina, with one butt joint (BJ), one finger joint (12mm, $FJ_{12}$) or one finger joint (4.5mm, $FJ_{4.5}$/) in tension side layer. Cryptomelia pieces were cut for butt and two finger types and glued with resorcinol-phenol resin adhesive. The results were as follows It was not effective in the bending modulus of elasicity (MOE) with IFJL type and had no difference from finger length. The bending modulus of rupture (MOR) of laminated wood beams including finger joint was the same values as that including butt feint and had no difference from finger length. It was effective in MOE with FJL type and had no difference from finger length. The effect of finger joint on MOR was much higher than that of butt joint but had no difference from finger length. The AE generation time of IFJL type was earlier than that of the control wood and the number of AE count was much more than that of the control wood. However, the AE generation time of FJL type was earlier than that of the control wood and the number of U count was much fewer than that of the control wood.

Our furniture industry is rapidly changing due to the declining economy. The existing weak furniture industry in Korea has yielded its inability to complete in a very competitive marketplace. The furniture companies lack the special necessary skills and professional knowledge necessary to design and manufacture furniture. Therefore, constant effort by designers and managers is needed in order to strengthen the Korean furniture industry's strategy and advance it into becoming a recognized player in the area of furniture design, worldwide, Designers has to have systematic training in order to have insight into upcoming international trends and incorporate new manufacturing techniques immediately This study will analyze the curriculums related to furniture design departments in Universities and technical schools in Germany, a leader in the furniture industry. It will present new educational ideas and program for furniture designers in the Korean universities.

This study was carried out to investigate the wood properties for development the proper uses of lesser-known tree species. The tested species are Tamiang(Hydnocarpus woodii) Bangelem (Strombosia zeylanica) and Kamasulan(Anisophyllea ferruginea) grown in Indonesia. fundamental wood properties such as anatomical, physical and chemical properties and characteristics related to wood processing were examined. The results are summarized as follows : These species are diffuse porous, interlocked grained and coarse textured wood. Exceptionally, texture of Tamiang is fine. The heartwoods of these species are not distinguished clearly to the sapwoods. These species have high specific gravity, high shrinkage, and excellent strength properties. However, Tamiang has moderate specific gravity. Sawing characteristics are poor for these species except Tamiang. Sawing characteristics is moderate for Tamiang. Drying characteristics are moderate for Tamiang and Bangelem, and Poor for Kamasulan. The surfacing characteristics by planer are moderate f3r all these species. Bending property and durability are poor. Ash content is low in Bangelem.

Ginkgo trees have long been planted in Korea as roadside trees and ornamental trees, but the wood was seldom used except some utilization f3r small artifacts. Soaring prices of imported wood and future uncertainty about long-term supply of foreign woods have stimulated research on value-added utilization of less-utilized domestic wood resources such as Ginkgo wood. The processing properties of Ginkgo wood were investigated to determine its utilization potential in this study, and the results of treatability, drying characteristics, gluability, paintability, bending properties, chemical discoloration characteristics were presented.

This study was carried out to determine the suitability of 3 months old bamboo species of Phyllostachys bambusoides S. et Z., Phyllostachys Pubescens Mazel and Phyllostachys nigra var henonis Stapf as raw materials for the manufacture of strandboard. Total of 108 strandboards were made using urea-formaldehyde resin content level of 12% and one percent of liquid wax emulsion. The strandboard consisted of three layers the top and the bottom layer of which were oriented to the same direction and weighted 25% of the strandboard each. The middle core layer weighed 50% of the board and was perpendicular to the outer top and bottom layers. Analysis was performed to determine the effect of strand lengths and Uowing years of 3 months, 2 years and 3 years on strandboard properties. The physical and mechanical properties of bamboo species and boards were measured and compared to the standard requirements of strandboards. The results are as follows; 1. The more the growing years the higher the density of bamboo. Top part of bamboo indicated higher density value than that of bottom part. 2. Bamboo showed higher static bending strength compared to the main wood species. Longer growing years of bamboo generally inclosed the static tending strength out there were no statistical significancies for Phyllostachys bmbusoides S. et Z. and Phyllostachys pubescens Mazel. 3. Strand length indicated no difference on density and moisture content of strandboard. 5 cm of strand length gave the best static bending strength and internal bonding strength. Bamboo strandboard exhibited lesser extents of thickness swelling than that of CSA standard. 4. 3 months old bamboo gave higher static bending strength of strandboard than those of 2 years and 3 years old bamboo. In case of Phyllostachys nigra var henonis Stapf, 3 months old bamboo indicated higher internal bonding strength than those of 2 years and 3years old bamboo. but in Phyllostachys bambusoides S. et Z., Phyllostachys pubescens Mazel, there were no difference among growing years. Growing years showed no different physical properties of bamboo strandboard.

Liquid ammonia treatment known as the most effective Wood plasticization method, was applied to two typical domestic species, Pinus densiflora, Castanea crenata. Small specimens of 30mm width, 300mm length and two thicknesses, 5 or 10mm, were used. For 5mm thick Specimens, Pinus densiflora was quite well plasticized iker 4 hour liquid ammonia treatment, while Castanea crenata was not plasticized even after 4 hour treatment. Specimens of 10mm thick Pinus densiflora were hardly plasticized, but those with kerfs were bent somewhat easily, With the increase of liquid ammonia treatment time the thermal conductivity of Pinus densiflora increased, while that of Castanea crenata didn't Presteaming before liquid ammonia treatment didn't improve the plasticization of both species.

The purpose of this study is to find out the current trend of tradition in Modern Korean Residential-furniture. Sample furniture of 374 pieces made by 21 manufacturers which have been shown in the market in September 2000, are selected for this study. To find out the traditional trend, frequency and percentage are used. As the result of the study, the major trend of design in Modern Korean Residential-furniture is modern style based on Modernism. However, it was found that there are tendency while large firms add western traditional elements in their furniture, small manufactures are trying to develop original furniture design which expresses Korean traditional characteristics. It means that the Korean traditional characteristics are not widely spread in Modern Residential-furniture.

Some physical characteristics as thickness swelling, heat conduction, and bending properties of composite hoards made of waste wood chip and charcoal were measured. Wood-charcoal composite boards of three types and cement board were prepared for this study as shown in Table 1, Keeping duration of strawberries in the boxes($25cm{\times}25cm{\times}25cm$) manufactured with the boards was also examined. Thickness swelling and bending properties(MOR and MOE) of board B and C were lower than those of board A. Among the wood-charcoal composite boards except cement board, there were no differences in heat conduction(mm/sec.). Strawberries in the box with board C were kept longer duration in fresh condition than that with cement board. From the results, it is suggested that wood-charcoal composite boards can be used for eco-material.

This study was carried out to measure formaldehyde emission with the passing of two years from plywood, sliver-board and strand-board bonded with urea resins which were made of 6 f/U molar ratios. The urea resins were manufactured by six kinds of formaldehyde/urea molar ratio of 1.0, 1.2, 1.4, 1.6, 1.8 and 2.0. 1. The plywood with molar ratio of 1.0 satisfied the KS F3101 $F_2$ directly after manufacture. The plywood with molar ratio of 1.2 satisfied m 3 days. The plywood with molar ratio of 1.4 satisfied the $F_3$ in 3 days and the $F_2$ in 600 days. And the plywood with molar ratio of 1.8 and 2.0 satisfied the $F_3$ in 365 days, but didn't satisfy the $F_2$ in 730 days. 2. Sliver-board with molar ratio of 1.0 and 1.2 satisfied the KS F3104 $E_2$ right after manufacture. Sliver-board with molar ratio of 1.4 and 1.6 satisfied in 150 and 360 days, respectively. Sliver-board with molar ratio of 1.8 and 2.0 satisfied in 730 days. 3. Strand-board with molar ratio of 1.0 and 1.2 satisfied the KS F3104$ E_2$ directly after manufacture. Strand-board with molar ratio of 1.4 and 1.6 satisfied in 150 days. But Strand-board with molar ratio of 1.8 and 2.0 didn't satisfied in 730 days.

It is well-known fact that dimensional stability of wood is greatly enhanced by acetylation of wood. This dimensional stability results from bulking of the reacted acetate within the cell wall, which reduces further swelling when the modified woods come into contact with water or water vapor. The purpose of this research was to determine the water absorption and dimensional stability of the acetylated solid wood in liquid water and in humidity tests. Beech and red oak were acetylated. Moisture and water absorption of acetylated wood were quite dependent on weight percent gain(WPG). Antiswelling efficiency(ASE) was quite dependent on WPG, but was not dependent on species.

furniture reflects historical, cultural, spatial background of human life style. This means that we cannot think of a furniture apart from the living environment. This study is focused on the process of furniture design in residential interiors. Furniture design process devided into the theoretical research the formal design process. Basically theoretical background contains human activities in place, antropometric data, requisite furniture type according to activities and some guidelines for design. And the formal design process is consisted of visual main concept, series of sketches and the development of alternatives of design. Thus, the theoretical background need to be applied to the steps of sketches, and for the harmonious interiors systematically.